POM 日本宝理 SF-10NC TD-10 聚甲醛塑胶原料
POM 物性表
性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | ||
机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
断裂伸长率 | ASTM D638/ISO 527 | 3 | % | |||
拉伸模量 | ASTM D638/ISO 527 | 10000 | kg/cm²(MPa)[Lb/in2] | |||
拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | % | ||||
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 190 | % | |||
弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | kg·cm/cm(J/M)ft·lb/in | ||||
弯曲强度 | ASTM D790/ISO 178 | kg·cm/cm(J/M)ft·lb/in | ||||
洛氏硬度 | ASTM D785 | |||||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in | ||
1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃（缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
23℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
-30℃（无缺口） | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||||
POM不耐强度和氧化剂，对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好，可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等，并可在高温下保持相当的化学稳定性。吸水性小，尺寸稳定性好。
POM的耐候性不好，长期在紫外线作用下，力学性能下降，表面发生粉化和龟裂。 结晶料,熔融范围窄，熔融和凝固快，料温稍低于熔融温度即发生结晶。流动性中等。吸湿小，可不经干燥处理。
- 薄壁产品应用POM 日本宝理 M270-12 M270-36 高流动性 2024-11-08
- POM20%须晶增强 日本宝理 KT-20 高强度材料 2024-11-08
- 聚甲醛 POM 日本宝理 HP25X HP90X 现货配送 2024-11-08
- 原包新料POM 日本宝理 DW-03A HC750 聚甲醛 2024-11-08
- 日本宝理 CW-01 低磨耗POM材料 2024-11-08
- yuantouchangjiaPOM 日本宝理 CP15X 高韧性 抗蠕变 2024-11-08
- POM 日本宝理 YF-5 加铁氟龙 PTFE%5 耐磨 2024-11-08
- POM 日本宝理 WR-01 防潮 低吸水率 2024-11-08
- 日本宝理聚甲醛 TC-20L VC-32 POM塑胶料信息 2024-11-08
- POM 日本宝理 NF-15R SF-15 聚甲醛材料物性表 2024-11-08